| 1 | Thickness (mm) | | 0.2–3.0 | 0.2–3.0 | 0.2–4.0 | 0.2–4.0 | |
| 2 | Width (m) | | 2.5–9.0 | 2.5–9.0 | 2.5–8.0 | 2.5–8.0 | |
| 3 | Tensile Strength (MD/TD) (MPa) | ≥ | 14 | 16 | 17 | 25 | |
| 4 | Elongation at Break (MD/TD) (%) | ≥ | 400 | 700 | 550 | 450 | 550 |
| 5 | Right Angle Tear Strength (N/mm) | ≥ | 50 | 60 | 60 | 80 | 110 |
| 6 | Water Vapor Transmission Rate (g·cm/cm²·s·Pa) | < | 1.0×10⁻⁰ | 1.0×10⁻⁰ | 1.0×10⁻⁰ | — | — |
| 7 | Operating Temperature Range | | +70℃ to -70℃ | +70℃ to -70℃ | +70℃ to -70℃ | — | — |
| 8 | Carbon Black Content (%) | | — | — | — | 2.0–3.0 | |
| 9 | Environmental Stress Cracking Resistance (F) | ≥ | — | — | — | 1500 | |
| 10 | Impact Brittleness at -70℃ | | — | — | — | Pass | |
| 11 | Oxidative Induction Time at 200℃ | | — | — | — | — | |